乙醇溶剂保护法制备非晶颗粒态玉米淀粉

基于乙醇溶剂具有抑制淀粉颗粒膨胀的特性,研究制备非晶颗粒态玉米淀粉的新方法。将玉米淀粉、水与乙醇按不同比例混合并在高温下反应,用偏光显微镜观测处理后的淀粉颗粒结构,结合X射线衍射曲线确认淀粉由多晶态向非晶态的变化。结果表明:当乙醇体积分数为50%,淀粉乳质量浓度为0.25 g/mL时,在85℃条件下反应,可以制备出质量较好的非晶颗粒态玉米淀粉。     

硫酸盐溶液渗析法制备非晶颗粒态玉米淀粉

硫酸钠作为保护剂,热处理原玉米淀粉,考察了硫酸钠加入时机,硫酸钠浓度及干燥方法对玉米淀粉非晶化的影响。用偏光显微镜观测处理后的淀粉样品,结合X射线衍射曲线验证淀粉颗粒结构的变化,利用扫描电镜观测淀粉颗粒,并宏观的观察处理后样品的状态。结果表明:用饱和硫酸钠配制淀粉样品,煮沸处理后,加入无水硫酸钠作渗析,冷冻干燥样品,原玉米淀粉可以均匀的转变为非晶颗粒态淀粉,且保持同原淀粉相同的干爽粉末状态。     

混合酸交联高温溶胀制备非晶颗粒态淀粉

采用已二酸和醋酸酯的混合酸交联处理玉米淀粉,然后对交联淀粉水浴加热至80℃制备非晶颗粒态淀粉.本文考察了不同的交联剂用量对玉米原淀粉非晶化的影响.用偏光显微镜观测处理后淀粉颗粒结构,结合X射线衍射曲线确认淀粉由多晶态向非晶态的变化.结果表明,当交联剂用量达到13%（淀粉干基）的时候,玉米淀粉可由多晶颗粒态的原淀粉制备出只含无定形结构的非晶颗粒态淀粉.     

环氧氯丙烷交联沸水溶胀制备非晶颗粒态淀粉

采用环氧氯丙烷高交联改性的方法处理玉米淀粉,然后对交联淀粉水浴加热至100℃制备非晶颗粒态淀粉.考察不同的交联剂用量对玉米原淀粉非晶化的影响.用偏光显微镜观测处理后淀粉颗粒结构,结合X射线衍射曲线确认淀粉由多晶态向非晶态的变化.结果表明,当交联剂环氧氯丙烷用量达到8.0%(淀粉干基)的时候,玉米淀粉可由多晶颗粒态的原淀粉制备出只含无定形结构的非晶颗粒态淀粉.     

非晶颗粒态玉米淀粉制备方法

系统地报道了水分散体系高温溶胀、常温碱分散体系强碱溶胀作用非晶颗粒态玉米淀粉制备方法,采用偏光显微镜对多晶态向非晶态的变化进行了确认,提出在一定条件下,高交联玉米淀粉可以由原淀粉多晶颗粒态制备成只含无定形结构的非晶颗粒态淀粉。     

甲醛交联高温溶胀法制备非晶颗粒态玉米淀粉

甲醛作为交联剂,高交联改性玉米淀粉后水域加热至78℃制备非晶颗粒态淀粉。考察不同的交联剂用量对原玉米淀粉非晶化的影响。用偏光显微镜观测处理后淀粉颗粒结构,结合X射线衍射曲线确认淀粉由多晶态向非晶态的变化。结果表明,当交联剂甲醛用量达到12.5%(淀粉干基)的时候,玉米淀粉可由多晶颗粒态的原淀粉制备出只含无定形结构的非晶颗粒态淀粉。     

以捏合机为反应器制备非晶颗粒态玉米淀粉

以捏合机为反应器,研究制备非晶颗粒态淀粉的新方法。将淀粉与水分按不同比例混合并在高温下反应,用偏光显微镜观测处理后的淀粉颗粒结构。结果表明,当淀粉与水分质量比为3∶6时,温度80℃维持30min,90%以上的原玉米淀粉多晶颗粒态转化成无定形结构的非晶颗粒态。     

热-醇处理制备非晶颗粒态葛根淀粉

为了获得非晶态的葛根淀粉颗粒,以乙醇为保护剂,考察了乙醇体积分数、料液比、非晶化处理温度及时间对葛粉非晶化的影响,用偏光显微镜观测处理后的淀粉颗粒结构。结果表明:当乙醇体积分数为50%,料液比为1︰4 (g/mL)时,在80℃条件下反应15 min,可以制备出质量较好的非晶颗粒态葛根淀粉。     

非晶颗粒态玉米淀粉老化特性

实验通过非晶颗粒态玉米淀粉不同环境下黏度变化分析其老化特性及其影响因素.结果表明:非晶颗粒态玉米淀粉糊静置贮藏过程中会发生老化现象,在4℃下老化比常温下快:非晶颗粒态玉米淀粉乳的临界浓度小于10%,13%～14%的淀粉乳,老化作用明显;加入葡萄糖和蔗糖均能促进非晶颗粒态玉米淀粉老化,浓度越大,老化效果越明显,老化后期高浓度蔗糖又抑制淀粉乳的老化;在偏酸或者偏碱的环境或无机盐存在,抑制非晶颗粒态玉米淀粉的老化.     

非晶颗粒态玉米淀粉理化性质及消化性能的研究

非晶颗粒态淀粉是一种特殊的淀粉物态形式,具有颗粒性,但不具有结晶性。为了实现对原淀粉颗粒的改性,本文以玉米淀粉为原料,采用乙醇溶液处理法制备非晶颗粒态淀粉。在此基础上,研究了这种非晶化处理方法对玉米淀粉的颗粒形貌、结晶性质、溶解度与膨胀力及体外消化性能的影响。结果表明,原淀粉经非晶化处理后颗粒性仍保持完整,但颗粒表面有较大爆裂孔生成,并出现明显褶皱;非晶颗粒态玉米淀粉呈现V-型衍射结构,其结晶性基本消失,颗粒由多晶颗粒态结构转变为非晶颗粒态结构;与玉米原淀粉相比,其溶解度和膨胀度在相同的测定温度下均明显增加。原淀粉经乙醇溶液处理后,其快消化淀粉含量由92.83%下降到81.64%。而慢消化淀粉和抗性淀粉总含量由7.17%上升到18.36%。因此,采用乙醇溶液处理法对淀粉颗粒进行改性将有助于开发低热量和慢血糖应答的产品。     

中等水分含量湿热处理对玉米淀粉颗粒非晶化的影响

控制中等水分含量,利用湿热处理的手段处理原玉米淀粉,考察了淀粉与水不同的质量比及处理温度对淀粉颗粒结构的影响。用偏光显微镜观测处理后淀粉样品以验证淀粉颗粒结构的变化,结合X射线衍射曲线验证淀粉颗粒结构的变化,利用扫描电镜观测颗粒保持的状态。结果表明:当淀粉浓度为65%时,80℃处理,原玉米淀粉可以均匀地转变为非晶颗粒态淀粉。     

微波辐射处理对玉米淀粉颗粒非晶化的影响

采用微波辐射的手.段处理原玉米淀粉,考察了分散剂种类,淀粉与分散剂的质量比及微波处理的温度对淀粉非晶化的影响。用偏光显微镜观测处理后淀粉的颗粒结构,结合X射线衍射曲线验证淀粉颗粒结构的变化,利用扫描电镜观測颗粒保持的状态。结果表明:当分散剂为水,淀粉与水分的质量比为3:4时,原玉米淀粉可以均匀的转变为非晶颗粒态淀粉。     

不同干燥工艺对非晶颗粒态玉米淀粉颗粒形貌的影响

非晶颗粒态淀粉是一种特殊的淀粉物态形式,具有颗粒性,但不具有结晶性,其具有较高的酶降解性、反应活性和吸附性能等。为了使非晶颗粒态淀粉工业化生产,对非晶淀粉颗粒进行了乙醇洗涤+常压烘箱干燥、真空烘箱干燥、常压烘箱干燥、真空冷冻干燥、喷雾干燥等不同干燥工艺。结果表明,不同的干燥工艺对非晶淀粉颗粒产生了不同的颗粒形貌。对其形貌的产生机理进行了科学的分析。     

Comparative susceptibilities of sago,potato and corn starches to alkali treatment

The effects of steeping starch (sago, corn, and potato), in 0.025 M of sodium hydroxide for 0, 15, and 30 days at 30 °C, on its granular structure and other physicochemical properties were investigated. Changes in the morphology of starch granules indicated that the alkaline solution affected the granular structure of the starch. Pasting studies showed that the peak viscosity, breakdown, and setback of sago and potato starch decreased significantly, whereas that of corn starch increased significantly, when steeping time was prolonged. Swelling power increased significantly for treated potato and corn starches, but it decreased for sago starch. The amylose content of all alkali-treated starches also decreased significantly after treatment. Onset and peak temperatures of gelatinization (as analyzed with a differential scanning calorimeter) increased significantly, but the enthalpy decreased, for both gelatinization and retrogradation. The results showed that the physicochemical properties of starch of various botanical origins were affected to variable degrees when it was treated with alkaline solution.     

氢氧化钠保护玉米淀粉过瘤胃效果研究

为探讨氢氧化钠保护玉米淀粉过瘤胃的效果,采用尼龙袋技术,通过0%、0.75%、1.5%氢氧化钠溶液喷洒处理粉碎和整粒玉米,发现氢氧化钠处理粉碎玉米与整粒玉米相比更能降低玉米的有效降解率.以0%、1.0%、2.0%、3.0%、4.0%、5.0%氢氧化钠溶液处理粉碎玉米发现,氢氧化钠处理可提高玉米的过瘤胃率,其用量以3.4%为宜.体外培养时,随着氢氧化钠水平的增加pH升高(P<0.05),氨态氮浓度差异不显著(P>0.05),挥发性脂肪酸总量升高(P<0.05),乙酸与丙酸比值下降(P<0.05).氢氧化钠处理通过改善瘤胃内环境,减缓淀粉的pH效应.     

玉米、木薯及马铃薯淀粉颗粒微晶结构及性质的研究

运用广角X射线衍射分析方法对玉米、木薯及马铃薯淀粉颗粒结晶结构及常温下水的溶胀作用对淀粉颗粒不同微晶结构的影响进行了系统研究,提出了在淀粉颗粒中存在着大量的介于微晶和非晶之间的亚微晶结构,并提供了在一条X射线衍射曲线图中确定微晶、亚微晶和非晶区域的方法。     

羟丙基糯玉米淀粉合成工艺及性能研究

本文以糯玉米淀粉为原料，以环氧丙烷为醚化剂、氢氧化钠为催化剂、硫酸钠为抑制膨胀剂，对糯玉米羟丙基淀粉合成工艺及其性能进行了研究，探讨了糯玉米淀粉乳浓度、环氧丙烷用量、反应时间、反应温度、氢氧化钠用量及硫酸钠用量对糯玉米羟丙基淀粉取代度和反应效率的影响。实验结果表明，增加环氧丙烷用量、延长反应时间，可使羟丙基淀粉取代度增加。对糯玉米羟丙基淀粉的冻融稳定性、透明度及粘度进行研究表明，随着羟丙基糯玉米淀粉取代度的增加，其冻融稳定性和透明度增加，但粘度却降低。     

乙酰化酸解糯玉米变性淀粉的制备及性能研究

以糯玉米淀粉为原料,盐酸为酸解剂,醋酸酐为酰化试剂,氢氧化钠为催化剂,无水硫酸钠为膨胀抑制剂,对乙酰化酸解糯玉米变性淀粉的制备工艺及性能进行研究。考察反应时间、反应温度、醋酸酐用量、pH值、无水硫酸钠用量对乙酰化酸解糯玉米变性淀粉取代度的影响。结果表明,各因素对酸解糯玉米淀粉的乙酰化 反应均有影响,最佳制备条件为反应温度25℃、反应时间50min、pH8.5、无水硫酸钠用量1.5%。酸解糯玉米淀粉经乙酰化后,其糊透明度、冻融稳定性均增加,且随着取代度的增大而增加,但乙酰化对凝沉性无影响。     

非晶颗粒态玉米淀粉制备羧甲基淀粉的研究

以原玉米淀粉、氯乙酸为主要原料,先用乙醇制备非晶颗粒态玉米淀粉,然后将氢氧化钠和氯乙酸加入反应瓶中制备羧甲基淀粉.研究了氯乙酸用量、氢氧化钠用量、反应体系水分含量、反应温度、时间对样品取代度(DS)的影响.结果表明:在m(氯乙酸)/m(淀粉)为0.2,n(氢氧化钠)/n(淀粉)为0.4,反应体系水分25%条件下,温度55℃反应4 h得到较高取代度的羧甲基淀粉CMS.